Dunting is a defect that appears
Answer: D
Correct answer: as cracks formed during cooling
Dunting is cracking caused by thermal or crystallographic stress during cooling - most often from cooling too fast through the quartz inversion, or from a draught striking part of the ware. The cracks are typically clean and sharp with no glaze rounding, which distinguishes them from cracks that were present before the peak.